Polymeric diols



United States Patent POLYMERIC DIOLS Alfred Coles Haven, Jr., Wilmington, Del., assignor to 5 E. I. du Pont de Nemours and Company, Wilmington, Del., a corporation of Delaware No Drawing. Original application February 9, 1956, Serial No. 564,351, now Patent No. 2,813,899, dated November 19, 1957. Divided and this application July 29, 1957, Serial No. 674,623

5 Claims. (Cl. 260-618) This invention is directed to the preparation of new compositions of matter which are essentially linear difunctional hydrocarbons of a molecular weight within the range of 500 to 3000.

Difunctional intermediates are necessary in the preparation of linear fibrous and elastomeric polymers. For example, condensation polymerization of dicarboxylic acids with diols or diamines leads to polyesters or polyamides. Similarly, polyurethanes may be obtained from glycols and diisocyanates.

It is an object of this invention to provide new polymeric hydroxy derivatives in which the hydroxy groups are separated by long hydrocarbon units.

More specifically, it is an object of the present invention to produce a difunctional compound of the formula XQ(A-B) -AQX, wherein X is CH OH; m is an integer from 1 to 4; A is a diradical formed by removing one hydrogen from each ring of a gem diphenylalkane; B is a C to C alkylene radical, having at least 3 carbon atoms in the bivalent alkylene unit, and Q is a C to C alkylene radical having at least 3 carbonatoms in its bivalent alkylene unit.

It has been discovered that difunctional hydrocarbons of molecular weight 500 to. 3000 may be obtained by coalkylating a gem diphenylalkane, e.g., diphenylmethane, with an unconjugated diene and an unconjugated unsaturated carboxylic acid, in certain molar proportions, in the presence of anhydrous hydrogen fluoride as condensing agent. The resulting polymeric dicarboxylic acids are substantially free of monoand polyfunctional side products and are readily reduced to the corresponding diols. These diols are suitable for the preparation of linear superpolymeric polyurethanes having elastomeric properties, by reaction with an organic diisocyanate followed by further chain extension with water. A gem diphenylalkane is a disubstituted compound wherein the disubstitution is carried out on the same carbon atom with two identical phenyl radicals. These dicarboxylic acids are disclosed and claimed in applicants copending divisional application Serial No. 564,351, filed February 9, 1956, now U.S. Patent 2,813,899, issued November 19, 1957.

The dicarboxylic acids may be prepared by co-alkylating, in the presence of liquid anhydrous hydrogen fluoride as condensing agent, It moles of a gem diphenylalkane (A) with a combination of nl moles of an unconjugated diolefin (B) having 6 to 21 carbon atoms, and 2 moles of an aliphatic unconjugated unsaturated carboxylic acid (Q) having from 4 to 18 carbon atoms,

n being an integer from 2 to 5.

The gem diphenylalkanes (A) may be represented by the formula C H -CR R C H where CR R is an alkylidene radical. R and R therefore may be H or alkyl; the alkyl radicals are preferably primary alkyl radicals. Gem diphenylalkanes may be prepared by condensing 2 moles of benzene with 1 mole of an ali- 7 phatic aldehyde or ketone. The total carbon content of the alkylidene radical will be limited primarily by the availability of the aldehydes and ketones. Those having up to 10 carbon atoms are readily accessible (e.g., from the corresponding alcohols); it is meant to include those gem diphenylalkanes, e.g., 1,1-diphenyldecane, which may be derived from them. For reasons of economy it is preferred to use gem'diphenylalkanes ranging'from the methane through the butanes with diphenylmethane the preferred compound. Other specific compounds which may be employed are: 1,1-diphenylethane; 1,1-diphenylpropane and 2,2-diphenylpropane; 1,1- and 2,2-diphenylbutanes including 1,1-diphenyl-2- methylpropane; 1,1-, 2,2-, and 3,3-diphenylpentanes and the corresponding hexanes; 1,1-, 2,2-, 3,3- and 4,4-diphenylheptanes and the corresponding members of the octane series; and the like.

To obtain the dicarboxylic acids substantially free of monoand polyfunctional acids both the diolefin (B) and the ethylenically unsaturated carboxylic acid (C) must be unconjugated; i.e., the unsaturated centers are separated by at least one and preferably 2 or more saturated carbon atoms. Furthermore, it is essential that anhydrous hydrogen fluoride be the condensing agent at temperatures below its normal boiling point and preferably at about 05 C.

Suitable unconjugated diolefins are found in the acyclic (straightor branched-chain) and in the alicyclic hydrocarbon series. Representative dienes having 6 to 21 carbon atoms and at least one saturated carbon atom separating the olefinically unsaturated groups are: 1,4- hexadiene, 1,5-hexadiene (biallyl); 1,4-heptadiene, 1,6- heptadiene; 2,6-octadiene, 4-methyl-l,5-heptadiene, 2,5- dimethyl-1,5-hexadiene; 2,7-nonodiene; 4,5-dimethy1-2,6- octadiene; 4-vinylcyclohexane, l-(3-butenyl)-l-cyclohexene; 1,15-hexadecadie ne, 1,18-nonodecadiene, 1,20-heneicosadiene, and the like.

In dienes of the alicyclic series, it is preferred that at least one of the ethylenically unsaturated groups be extranuclear, e.g., as in 4-vinylcyclohexene and in l-allylcyclopentene. It is also preferred that at least 2 saturated carbon atoms separate the olefinic groups, e.g., as in 1,5-hexadiene, 1,15-hexadecadiene and the like.

Conjugated dienes and alpha,beta-unsaturated carboxylic acids are unsatisfactory as they homopolyrnerize under the conditions of our process to extraneous polymeric substances. These secondary reactions, in depleting the available supply of diolefin and/or of unsaturated acid, drastically alter the mole ratios of the reactants that are needed to yield dicarboxylic acids.

Suitable unsaturated carboxylic acids may be represented by the formula RCO H, where R is an unsaturated aliphatic hydrocarbon radical of from 3 to 17 carbons, where the carboxyl group is separated from the ethylenic double bond by at least one saturated carbon atom and preferably by 2 or more saturated carbon atoms. R may be an alkenyl or cycloalkenyl radical; it may be a cycloalkenyl-substituted alkyl group (as distinguished from an alkenyl-substituted alkyl group or an alkyl-substituted alkenyl group which are mere homologs of an alkenyl radical); it may be an alkylor cycloalkyl-substituted cycloalkenyl group. As indicated above, R is attached to the carboxyl group through one or more saturated carbon atoms. Examples of specific unconjugated unsaturated carboxylic acids are: 3-butenoic, 3- and 4- pentenoic, 2-methyl-3-pentenoic, 3-methyl-3-butenoic, 3-, 4-, and S-hexenoic, 4-methyl-3-pentenoic, 6-heptenoic, 5- methyl-4-hexenoic, 3-ethyl-3-pentenoic, 7-octenoic, 2- ethyl-3-hexenoic, 8-nonenoic, 7-, 8-, 9- and 10-undecenoic acids; 2-cyclopentene carboxylic acid, 2-cyclopentenylacetic acid, 3-cyclohexene carboxylic acid, cyclohexenylacetic acid, 7-cycloheptylidene-heptanoic acid, 6-cyclohexyl-S-hexenoic acid, and octadecenoic acids such as 3 oleic and elaidic acids. Preferred acids are IO-undecenoic acid and oleic acid.

The present invention in its simplest form is defined by 11:2; that is, reaction-of 2 moles of A with 1 mole of B and 2 moles of Q. yields dicarboxylic acids of the formula XQ-(A-B),,;-+A'QT'-=X,' where, m=1. Structures of A, B and Q may be varied as defined to produce a variety of these dicarboxylic acids. The smallest member of this series, corresponding to amolecular Weight of 592, is derived from 2 moles of diph'enylmethane, 1 mole of biallyl and 2 molesof 3-butenoic acid. The invention is also adapted to. the preparation of more complex structures. Thus; inaaddition to. varying the chemical nature of A, B and Q; themole ratios of these reactants may be varied so that n =2, 3, 4, or 5. A practical limit for obtaining dicarboxylic acids represented by the above formula is reached when n=5., When n is greater'than 5, the carboxylic acids produced are no longer substantially free of rtionoand/orpolyfunctional compounds, as indi'catedby the failure of these carboxylic acids to produce linear polymers; instead, gelled, i.e., three dimensional structures are formed. ,.As.stated, successful coalkylation of a gem diphenylalkane (A). with diolefin (B, defined)v and unsaturatedacid (Q, as defined), in molar ratios of A:B:Q of n: (11-1) :2, where n =2 to 5, depends upon the use of liquid anhydrous hydrogen fluoride as the condensing agent. Coalkylation of A by B and Q proceeds smoothly in HF to give substantially pure products in excellent yields;

According to the present invention, a ger'ndiphenylalkane, a diolefin and an unsaturated acid as defined, are used in mole ratios providing one ethylenically unsaturated center for each phenyl ring to be alkylated; there are at least two phenyl rings for each molecule of unsaturated carboxy acid. t

The dicarboxylic acids have relatively high molecular weights, low volatility, and are either difficult to distill or not distillable; they tend to'be viscous liquids and are diflicult to crystallize: It is therefore highly desirable to be able to avoid tedious and costly separation and purification steps in recovering them from the reaction mixture. These objects are achieved by using hydrogen fluoride as the condensing agent in the preparative reaction.

These dicarboxylic acids are prepared by adding a mixture of the proper proportions of a gem diphenylalkane, a diolefin and an unsaturated acid to an excess of anhydrous hydrogen fluoride below the normal boiling point of HF, preferably at Oto C. The reaction mass is worked up by drowning the charge in water and taking up the reaction product in an organic solvent which is immiscible with water and which is sufficiently volatile to be recovered by distillation, e.g., benzene, ethyl ether, petroleum ether or mixtures of these and the like. The organic layer is washed free of hydrofluoric acid with water, and then evaporated in vacuo to yield the desired dicarboxylic acids.

Hydrogen fluoride has the unique advantage over other typical Friedel-Crafts catalysts such as aluminum chloride, ferric chloride, titanium chloride, etc., in being an extremely efficient catalyst for alkylations at temperatures that are low enough to suppress secondary reactions leading to complex cross-linked and tarry products.

The dicarboxylic acids formed are reduced to the corresponding diols (X= CH OH in thestructural representation) in high yields. These diols, in turn, may be converted into polymeric products, e.g., polyesters or polyurethane s, on reaction with polyacids (or polyacid chlorides) or organic polyisocyanates. Using a di isocyanate, such as toluene-2,4-diisocyanate, for example, linear polyurethanes are obtained, By linear is meant extended, chainlike, polymers as distinguished from three-dimensional, crosslinked structures. That these polyurethanes are substantially free from the cross linked (gelled) structures is shown by their-ready solubility in a solvent such as tetrahydrofuran. The intrinsic viscosities of these solutions show that the solutes are polymeric; the original dicarboxylic acids from which said diols are produced are substantially free of triand poly-functionality.

EX AM 1 in 1 A. A mixture consisting of:

16.8' g. (0.1 mole) diphenylmethane 18.5 g. (0.1)mole) IO-unde'cylenic acid 5.4 g. (0.05 mole) 4-vinylcyc1ohexene Analyses" Found Required by theory 26 Carbon Hydrnnnn Neutral Equiv 1 Calculated for the dibasic acid of molecular weight 813.2.

B. A mixture of 36.3 g. of the abeve product, '8 g. of lithium aluminum hydride and 500 must tetrahydrofuran was held at its reflux temperature for 2 Hours. The mixture was cooled to 0 C. and treated with s'ufiicient saturated aqueous ammonium chloride solution to destroy any unreac't'ed LiAlH, and to liberate the reduction product from its complexes with aluminum. The mass was filtered and the cake of inorganic salts was washed with small quantities of tetrahydrofuran. The organic solution of the combined filtrate and washings was evaporated in vacuo, finally at 100 C. and 1 inm. of Hg to obtain 34.5 g. of the glycol.

Analyses Found Required by theory 84. er o s5. 4 16223/1628' 0. es

1 Calculated for 055E500}, glycol of molecular weight 786.

C. A mixture of 22.4 g. of the above glycol and 8.5 g. of toluene 2,4-diisocyanate (corresponding to a mole ratio of diisocyanate to glycol of 1.5 to l) was heated at 100 C. for 3 hours. The product, a viscous liquid, was dissolved in 100 ml. tetrahydrofuran. This solution was treated with one gram of water (corresponding to. 9 times the theoretical quantity necessary to convert the free isocyanate groups in the polymer into urea groups and thus further extend the chain length) and allowed to stand at room temperature for 72 hours. No insoluble gel formed, indicating absence of trifunctionality in the polymer. The solution was allowed to evaporate in a pan. The residue was worked on a rubber mill at 100 C. to volatilize residual traces of tetrahydrofuran and then milled to give a sheet of raw stock having an elongation before break of 100 to 200%.

EXAMPLE 2 A. A mixture consisting of:

Analyses Found Required by theory 1 Carbon 82. 83. 0 Hydro en 10. 6 10. N eutral-E quiv 609 498. 5

1 Calculated for a dibasic acid of empirical formula CusH104O molecular weight 997.

B. A solution of 42.8 g. of the above condensation product in 100 ml. tetrahydrofuran was slowly added to a refluxing solution of 8 g. of lithium aluminum hydride in 300 ml. tetrahydrofuran. The reaction mass stirred and held at its temperature of reflux for one hour, then cooled to about 0 C. Saturated aqueous ammonium chloride was added in sufiicient quantity to precipitate all of the aluminum as inorganic salts, and the mass was filtered. The filter cake of inorganic material was washed with small quantities of benzene and the combined organic filtrate and washings were concentrated at 100 C. and less than 1 mm. of Hg pressure to an oil weighing 39.7 g.

Analyses Found Required by theory 1 Carbon 83. 8 85. 5 Hydrogen 11. 1 11. 25 Hydroxyl-N umber- 123 116 Acid-N umber 0. 13

1 Calculated for a glycol of molecular weight 969 and having an empirical formula OasHrosOa.

C. The glycol obtained under B above was converted into an elastomeric polyurethane as follows: 22.75 g. of glycol and 8.7 g. of toluene-2,4-diisocyanate (mole ratio of diisocyanate to glycol=2 to 1) were mixed and held at 75 C. for 20 minutes. Twd ml. of water were blended into the resulting viscous liquid and the mass was baked at 80 C. for one hour. Milling on a rubber mill gave a tough, flexible sheet of polyurethane elastomer which was readily soluble in tetrahydrofuran.

A strip 1.5 x 7.5 cm. of this polyurethane was so weighted that in 5 hours it had elongated to 34.5 cm. (366% elongation). On standing overnight, with the weights removed, it contracted to a length of 16 cm.

EXAMPLE 3 A mixture of:

22.25 g. (0.1 mole) 1,15-hexadecadiene 33.6 g. (0.2 mole) diphenylmethane 368 g. (0.2 mole) IO-undecenoic acid (98% yield).

EXAMPLE 4 A mixture of:

33.6 g. (0.2 mole) diphenylmethane 56.5 g. (0.2 mole) oleic acid 29.2 g. (0.1 mole) 1,20-heneicosadiene was added to ml. anhydrous hydrogen fluoride over a one-hour period at 0-5 C. The reaction mass was worked up as described previously to yield 114 g. of oily, liquid dicarboxylic acid.

A portion of this product was reduced with lithium aluminum hydride (following the procedures of the previous examples) to the corresponding glycol. The hydroxyl-number of 104 for this glycol corresponds to a calculated molecular weight of 1080, in fair agreement with a molecular weight of 1164 for a glycol of empirical formula C83H133O3.

A 43.4 g. sample of this glycol was heated for one hour at 100 C. with 14.1 g. of toluene-2,4-diisocyanate. The product was dissolved in 300 ml. tetrahydrofuran, one ml. of water was added, and the solution allowed to stand at room temperature. At the end of 8 days, no gel had formed. One ml. of piperidine was added to destroy any remaining free isocyanate groups and the solution was evaporated to constant weight in vacuo at 100 C. to obtain 55.5 g. of the polyurethane.

EXAMPLE 5 The followingmixture:

9.25 g. (0.05 mole) IO-undecenoic acid 21.0 g. (0.125 mole) diphenylmethane 10.8 g. (0.10 mole) 4-vinylcyclohexene was added dropwise to 100 ml. anhydrous HP at 0-5" C. After 75 minutes the mixture was poured onto ice and extracted with ethyl ether. The extract, after being washed with water to remove HF, was evaporated in vacuo at 100 C. to give 40.4 g. of an oil consisting of a mixture of dicarboxylic acids.

According to the procedures described in previous examples, this product was reduced with 6 g. of lithium aluminum hydride in 600 ml. tetrahydrofuran to the corresponding glycol, a viscous oil weighing 38.5 g.

EXAMPLE 6 Following the procedure given in Example 5, 9.25 g. (0.05 mole) of IO-undecenoic acid, 21 g. (0.125 mole) of disphenylmethane and 8.2 g. (0.10 mole) biallyl, added to 100 ml. anhydrous HF gave a substantially quantitative yield of liquid dicarboxylic acid.

The embodiments of the invention in which an exclusive property or privilege is claimed are defined as follows:

1. A difunctional compound of the general formula XQ-(AB),,,-AQ-X, wherein X is CH OH; m is an integer from 1 to 4; A is a diradical formed by removing one hydrogen from each ring of a gem diphenylalkane having 1 to 10 carbon atoms in the alkylidene radical; B is an alkylene radical bridging said diradicals A and contains from 6 to 21 carbon atoms, at least 3 carbon atoms being in the bivalent alkylene chain, and; Q is an alkylene radical containing from 3 to 17 carbon atoms, at least 3 carbon atoms being in the bivalent a1- kylene chain.

2. A difunctional compound of the general formula set forth in claim 1 wherein m is 1.

3. A difunctional compound of the general formula set forth in claim 1 wherein A is diphenylmethane.

4. A difunctional compound of the general formula set forth in claim 1 wherein B is vinylcyclohexene.

5. A difunctional compound of the general formula set forth in claim 1 wherein Q is a C alkylene radical.

References Cited in the file of this patent UNITED STATES PATENTS 2,555,918 Cofiman et a1. June 5, 1951 2,576,311 Schlesinger et a1. Nov. 27, 1951 2,794,822 Schweitzer June 4, 1957 2,813,899 Haven Nov. 19, 1957 

1. A DIFUNCTIONAL COMPOUND OF THE GENERAL FORMULA X-Q-(A-B)M-A-Q-X, WHEREIN X IS-CH2OH, M IS AN INTEGER FROM 1 TO 4, A IS A DIRADICAL FORMED BY REMOVING ONE HYDROGEN FROM EACH RING OF A GEM DIPHENYLALKANE HAVING 1 TO 10 CARBON ATOMS IN THE ALKYLIDENE RADICAL, B IS AN ALKYLENE RADICAL BRIDGING SAID DIRADICALS A AND CONTAINS FROM 6 TO 21 CARBON ATOMS, AT LEAST 3 CARBON ATOMS BEING IN THE BIVALENT ALKYLENE CHAIN, AND, Q IS AN ALKYLENE RADICAL CONTAINING FROM 3 TO 17 CARBON ATOMS, AT LEAST 3 CARBON ATOMS BEING IN THE BIVALENT ALKYLENE CHAIN 